Allotropy

Short description: Property of some chemical elements to exist in two or more different forms

Diamond and graphite are two allotropes of carbon: pure forms of the same element that differ in crystalline structure.

Allotropy or allotropism (from grc ἄλλος (allos) 'other', and τρόπος (tropos) 'manner, form') is the property of some chemical elements to exist in two or more different forms, in the same physical state, known as allotropes of the elements. Allotropes are different structural modifications of an element: the atoms of the element are bonded together in different manners.[1] For example, the allotropes of carbon include diamond (the carbon atoms are bonded together to form a cubic lattice of tetrahedra), graphite (the carbon atoms are bonded together in sheets of a hexagonal lattice), graphene (single sheets of graphite), and fullerenes (the carbon atoms are bonded together in spherical, tubular, or ellipsoidal formations).

The term allotropy is used for elements only, not for compounds. The more general term, used for any compound, is polymorphism, although its use is usually restricted to solid materials such as crystals. Allotropy refers only to different forms of an element within the same physical phase (the state of matter, such as a solid, liquid or gas). The differences between these states of matter would not alone constitute examples of allotropy. Allotropes of chemical elements are frequently referred to as polymorphs or as phases of the element.

For some elements, allotropes have different molecular formulae or different crystalline structures, as well as a difference in physical phase; for example, two allotropes of oxygen (dioxygen, O2, and ozone, O3) can both exist in the solid, liquid and gaseous states. Other elements do not maintain distinct allotropes in different physical phases; for example, phosphorus has numerous solid allotropes, which all revert to the same P4 form when melted to the liquid state.

## Contents

* 1 History
* 2 Differences in properties of an element's allotropes
* 3 List of allotropes
* 3.1 Non-metals
* 3.2 Metalloids
* 3.3 Metals
* 3.3.1 Lanthanides and actinides
* 4 Nanoallotropes
* 5 See also
* 6 Notes
* 7 References
* 8 External links

## History

The concept of allotropy was originally proposed in 1840 by the Swedish scientist Baron Jöns Jakob Berzelius (1779–1848).[2][3] The term is derived from gre άλλοτροπἱα (allotropia) 'variability, changeableness'.[4] After the acceptance of Avogadro's hypothesis in 1860, it was understood that elements could exist as polyatomic molecules, and two allotropes of oxygen were recognized as O2 and O3.[3] In the early 20th century, it was recognized that other cases such as carbon were due to differences in crystal structure.

By 1912, Ostwald noted that the allotropy of elements is just a special case of the phenomenon of polymorphism known for compounds, and proposed that the terms allotrope and allotropy be abandoned and replaced by polymorph and polymorphism.[5][3] Although many other chemists have repeated this advice, IUPAC and most chemistry texts still favour the usage of allotrope and allotropy for elements only.[6]

## Differences in properties of an element's allotropes

Allotropes are different structural forms of the same element and can exhibit quite different physical properties and chemical behaviours. The change between allotropic forms is triggered by the same forces that affect other structures, i.e., pressure, light, and temperature. Therefore, the stability of the particular allotropes depends on particular conditions. For instance, iron changes from a body-centered cubic structure (ferrite) to a face-centered cubic structure (austenite) above 906 °C, and tin undergoes a modification known as tin pest from a metallic form to a semimetallic form below 13.2 °C (55.8 °F). As an example of allotropes having different chemical behaviour, ozone (O3) is a much stronger oxidizing agent than dioxygen (O2).

## List of allotropes

Typically, elements capable of variable coordination number and/or oxidation states tend to exhibit greater numbers of allotropic forms. Another contributing factor is the ability of an element to catenate.

Examples of allotropes include:

### Non-metals

Element  | Allotropes

|

Carbon |

* Diamond – an extremely hard, transparent crystal, with the carbon atoms arranged in a tetrahedral lattice. A poor electrical conductor. An excellent thermal conductor.
* Lonsdaleite – also called hexagonal diamond.
* Graphene – is the basic structural element of other allotropes, nanotubes, charcoal, and fullerenes.
* Q-carbon – a ferromagnetic, tough, and brilliant crystal structure that is harder and brighter than diamonds.[dubious - discuss]
* Graphite – a soft, black, flaky solid, a moderate electrical conductor. The C atoms are bonded in flat hexagonal lattices (graphene), which are then layered in sheets.
* Linear acetylenic carbon (carbyne)
* Amorphous carbon
* Fullerenes, including buckminsterfullerene, also known as "buckyballs", such as C60.
* Carbon nanotubes – allotropes having a cylindrical nanostructure.
* Schwarzites
* Cyclocarbon
* Glassy carbon
* Superdense carbon allotropes – proposed allotropes

Nitrogen |

* Dinitrogen – by far the most common and stable form of nitrogen, found in the air.
* Hexazine
* Octaazacubane
* Tetranitrogen
* Trinitrogen
* Solid nitrogen

Phosphorus |

* White phosphorus – crystalline solid of tetraphosphorus (P4) molecules
* Red phosphorus – amorphous polymeric solid
* Scarlet phosphorus
* Violet phosphorus with monoclinic crystalline structure
* Black phosphorus – semiconductor, analogous to graphite
* Diphosphorus – gaseous form composed of P2 molecules, stable between 1200 °C and 2000 °C; created e.g. by dissociation of P4 molecules of white phosphorus at around 827 °C

Oxygen |

* Dioxygen, O2 – colorless (faint blue liquid and solid)
* Ozone, O3 – blue
* Tetraoxygen, O4 – metastable
* Octaoxygen, O8 – red

Sulfur |

* Cyclo-Pentasulfur, Cyclo-S5
* Cyclo-Hexasulfur, Cyclo-S6
* Cyclo-Heptasulfur, Cyclo-S7
* Cyclo-Octasulfur, Cyclo-S8

Selenium |

* "Red selenium", cyclo-Se8
* Gray selenium, polymeric Se
* Black selenium, irregular polymeric rings up to 1000 atoms long
* Monoclinic selenium, dark red transparent crystals

### Metalloids

Element  | Allotropes

|

Boron |

* Amorphous boron – brown powder – B12 regular icosahedra
* α-rhombohedral boron
* β-rhombohedral boron
* γ-orthorhombic boron
* α-tetragonal boron
* β-tetragonal boron
* High-pressure superconducting phase

Silicon |

* Amorphous silicon
* Crystalline silicon, diamond cubic structure
* Silicene, buckled planar single layer Silicon, similar to Graphene

Germanium |

* α-germanium – semimetallic, with the same structure as diamond
* β-germanium – metallic, with the same structure as beta-tin
* Germanene – Buckled planar Germanium, similar to graphene

Arsenic |

* Yellow arsenic – molecular non-metallic As4, with the same structure as white phosphorus
* Gray arsenic, polymeric As (metallic, though heavily anisotropic)
* Black arsenic – molecular and non-metallic, with the same structure as red phosphorus

Antimony |

* Blue-white antimony – stable form (metallic), with the same structure as gray arsenic
* Black antimony (non-metallic and amorphous, only stable as a thin layer)

Tellurium |

* Amorphous tellurium – gray-black or brown powder[7]
* Crystalline tellurium – hexagonal crystalline structure (metalloid)

### Metals

Among the metallic elements that occur in nature in significant quantities (56 up to U, without Tc and Pm), almost half (27) are allotropic at ambient pressure: Li, Be, Na, Ca, Ti, Mn, Fe, Co, Sr, Y, Zr, Sn, La, Ce, Pr, Nd, Sm, Gd, Tb, Dy, Yb, Hf, Tl, Th, Pa and U. Some phase transitions between allotropic forms of technologically relevant metals are those of Ti at 882 °C, Fe at 912 °C and 1394 °C, Co at 422 °C, Zr at 863 °C, Sn at 13 °C and U at 668 °C and 776 °C.

Element  | Phase name(s)  | Space group  | Pearson symbol | Structure type  | Description

|
|
|
|
|

Lithium | α-Li  | R3m  | hR9  | α-Sm | Forms below 70 K.[8]
β-Li  | Im3m  | cI2  | W | Stable at room temperature and pressure.
| Fm3m  | cF4  | Cu | Forms above 7GPa
| R3m  | hR1  | α-Hg | An intermediate phase formed ~40GPa.[9]
| I43d  | cI16  |  | Forms above 40GPa.[9]
|  | oC88  |  | Forms between 60 and 70 GPa.[10]
|  | oC40  |  | Forms between 70 and 95 GPa.[10]
|  | oC24  |  | Forms above 95 GPa.[10]
Beryllium | α-Be  | P63/mmc  | hP2  | Mg | Stable at room temperature and pressure.
β-Be  | Im3m  | cI2  | W | Forms above 1255 °C.
Sodium | α-Na  | R3m  | hR9  | α-Sm | Forms below 20 K.
β-Na  | Im3m  | cI2  | W | Stable at room temperature and pressure.
| Fm3m  | cF4  | Cu | Forms at room temperature above 65 GPa.[11]
| I43d  | cI16  |  | Forms at room temperature, 108GPa.[12]
| Pnma  | oP8  | MnP  | Forms at room temperature, 119GPa.[13]
|  | tI19*  |  | A host-guest structure that forms above between 125 and 180 GPa.[10]
|  | hP4  |  | Forms above 180 GPa.[10]
Magnesium |  | P63/mmc  | hP2  | Mg | Stable at room temperature and pressure.
| Im3m  | cI2  | W | Forms above 50 GPa.[14]
Aluminium | α-Al  | Fm3m  | cF4  | Cu | Stable at room temperature and pressure.
β-Al  | P63/mmc  | hP2  | Mg | Forms above 20.5 GPa.
Potassium |  | Im3m  | cI2  | W | Stable at room temperature and pressure.
| Fm3m  | cF4  | Cu | Forms above 11.7 GPa.[10]
| I4/mcm  | tI19*  |  | A host-guest structure that forms at about 20 GPa.[10]
| P63/mmc  | hP4  | NiAs | Forms above 25 GPa.[10]
| Pnma  | oP8  | MnP  | Forms above 58GPa.[10]
| I41/amd  | tI4  |  | Forms above 112 GPa.[10]
| Cmca  | oC16  |  | Formas above 112 GPa.[10]
Iron | α-Fe, ferrite | Im3m  | cI2  | Body-centered cubic  | Stable at room temperature and pressure. Ferromagnetic at T<770 °C, paramagnetic from T=770–912 °C.
γ-iron, austenite | Fm3m  | cF4  | Face-centered cubic  | Stable from 912 to 1,394 °C.
δ-iron  | Im3m  | cI2  | Body-centered cubic  | Stable from 1,394 – 1,538 °C, same structure as α-Fe.
ε-iron, Hexaferrum | P63/mmc  | hP2  | Hexagonal close-packed  | Stable at high pressures.
Cobalt[15] | α-Cobalt  |  |  | hexagonal-close packed | Forms below 450 °C.
β-Cobalt  |  |  | face centered cubic | Forms above 450 °C.
ε-Cobalt  | P4132  |  | primitive cubic | Forms from thermal decomposition of [Co2CO8]. Nanoallotrope.
Rubidium | α-Rb  | Im3m  | cI2  | W | Stable at room temperature and pressure.
|  | cF4  |  | Forms above 7 GPa.[10]
|  | oC52  |  | Forms above 13 GPa.[10]
|  | tI19*  |  | Forms above 17 GPa.[10]
|  | tI4  |  | Forms above 20 GPa.[10]
|  | oC16  |  | Forms above 48 GPa.[10]
Tin | α-tin, gray tin, tin pest | Fd3m  | cF8  | d-C | Stable below 13.2 °C.
β-tin, white tin  | I41/amd  | tI4  | β-Sn  | Stable at room temperature and pressure.
γ-tin, rhombic tin  | I4/mmm  | tI2  | In | Forms above 10 GPa.[16]
γ'-Sn  | Immm  | oI2  | MoPt2 | Forms above 30 GPa.[16]
σ-Sn, γ"-Sn  | Im3m  | cI2  | W | Forms above 41 GPa.[16] Forms at very high pressure.[17]
δ-Sn  | P63/mmc  | hP2  | Mg | Forms above 157 GPa.[16]
Stanene |  |  |  |
Polonium | α-Polonium  |  |  | simple cubic |
β-Polonium  |  |  | rhombohedral  |

Template:Colorsample Most stable stable under standard conditions.
Template:Colorsample Structures stable below room temperature.
Template:Colorsample Structures stable above room temperature.
Template:Colorsample Structures stable above atmospheric pressure.

#### Lanthanides and actinides

Phase diagram of the actinide elements.

* Cerium, samarium, dysprosium and ytterbium have three allotropes.
* Praseodymium, neodymium, gadolinium and terbium have two allotropes.
* Plutonium has six distinct solid allotropes under "normal" pressures. Their densities vary within a ratio of some 4:3, which vastly complicates all kinds of work with the metal (particularly casting, machining, and storage). A seventh plutonium allotrope exists at very high pressures. The transuranium metals Np, Am, and Cm are also allotropic.
* Promethium, americium, berkelium and californium have three allotropes each.[18]

## Nanoallotropes

In 2017, the concept of nanoallotropy was proposed by Rafal Klajn of the Organic Chemistry Department of the Weizmann Institute of Science.[19] Nanoallotropes, or allotropes of nanomaterials, are nanoporous materials that have the same chemical composition (e.g., Au), but differ in their architecture at the nanoscale (that is, on a scale 10 to 100 times the dimensions of individual atoms).[20] Such nanoallotropes may help create ultra-small electronic devices and find other industrial applications.[20] The different nanoscale architectures translate into different properties, as was demonstrated for surface-enhanced Raman scattering performed on several different nanoallotropes of gold.[19] A two-step method for generating nanoallotropes was also created.[20]

## See also

* Isomer
* Polymorphism (materials science)

## Notes

1. ↑ IUPAC, Compendium of Chemical Terminology, 2nd ed. (the "Gold Book") (1997). Online corrected version:  (2006-) "Allotrope". doi:10.1351/goldbook.A00243
2. ↑ See:
* Berzelius, Jac. (1841) (in Swedish). Årsberättelse om Framstegen i Fysik och Kemi afgifven den 31 Mars 1840. Första delen.. Stockholm, Sweden: P.A. Norstedt & Söner. p. 14. https://babel.hathitrust.org/cgi/pt?id=nyp.33433009789326&view=1up&seq=176. From p. 14: "Om det ock passar väl för att uttrycka förhållandet emellan myrsyrad ethyloxid och ättiksyrad methyloxid, så är det icke passande för de olika tillstånd hos de enkla kropparne, hvari dessa blifva af skiljaktiga egenskaper, och torde för dem böra ersättas af en bättre vald benämning, t. ex. Allotropi (af αλλότροπος, som betyder: af olika beskaffenhet) eller allotropiskt tillstånd." (If it [i.e., the word isomer] is also well suited to express the relation between formic acid ethyl oxide [i.e., ethyl formate] and acetic acid methyloxide [i.e., methyl acetate], then it [i.e., the word isomers] is not suitable for different conditions of simple substances, where these [substances] transform to have different properties, and [therefore the word isomers] should be replaced, in their case, by a better chosen name; for example, Allotropy (from αλλότροπος, which means: of different nature) or allotropic condition.)
* Republished in German: Berzelius, Jacob; Wöhler, F., trans. (1841). "Jahres-Bericht über die Fortschritte der physischen Wissenschaften" (in German). Jahres Bericht Über die Fortschritte der Physischen Wissenschaften (Tübingen, (Germany): Laupp'schen Buchhandlung) 20: 13. https://babel.hathitrust.org/cgi/pt?id=umn.31951d000120766&view=1up&seq=189. From p. 13: "Wenn es sich auch noch gut eignet, um das Verhältniss zwischen ameisensaurem Äthyloxyd und essigsaurem Methyloxyd auszudrücken, so ist es nicht passend für ungleiche Zustände bei Körpern, in welchen diese verschiedene Eigenschaften annehmen, und dürfte für diese durch eine besser gewählte Benennung zu ersetzen sein, z. B. durch Allotropie (von αλλότροπος, welches bedeutet: von ungleicher Beschaffenheit), oder durch allotropischen Zustand." (Even if it [i.e., the word isomer] is still well suited to express the relation between ethyl formate and methyl acetate, then it is not appropriate for the distinct conditions in the case of substances where these [substances] assume different properties, and for these, [the word isomer] may be replaced with a better chosen designation, e.g., with Allotropy (from αλλότροπος, which means: of distinct character), or with allotropic condition.)
* Merriam-Webster online dictionary: Allotropy
3. ↑ 3.0 3.1 3.2 Jensen, W. B. (2006), "The Origin of the Term Allotrope", J. Chem. Educ. 83 (6): 838–39, doi:10.1021/ed083p838, Bibcode: 2006JChEd..83..838J .
4. ↑ "allotropy", A New English Dictionary on Historical Principles, 1, Oxford University Press, 1888, p. 238 .
5. ↑ Ostwald, Wilhelm; Taylor, W.W., trans. (1912). Outlines of General Chemistry (3rd ed.). London, England: Macmillan and Co., Ltd.. p. 104. https://books.google.com/books?id=1w1DAAAAIAAJ&pg=PA104. From p. 104: "Substances are known which exist not only in two, but even in three, four or five different solid forms; no limitation to the number is known to exist. Such substances are called polymorphous. The name allotropy is commonly employed in the same connexion, especially when the substance is an element. There is no real reason for making this distinction, and it is preferable to allow the second less common name to die out."
6. ↑ Jensen 2006, citing Addison, W. E. The Allotropy of the Elements (Elsevier 1964) that many have repeated this advice.
7. ↑ Raj, G.. Advanced Inorganic Chemistry Vol-1. Krishna Prakashan. p. 1327. ISBN 9788187224037. https://books.google.com/books?id=0uwDTrxyaB8C&pg=PA1327. Retrieved January 6, 2017.
8. ↑ Overhauser, A. W. (1984-07-02). "Crystal Structure of Lithium at 4.2 K". Physical Review Letters (American Physical Society (APS)) 53 (1): 64–65. doi:10.1103/physrevlett.53.64. ISSN 0031-9007. Bibcode: 1984PhRvL..53...64O.
9. ↑ 9.0 9.1 Hanfland, M.; Syassen, K.; Christensen, N. E.; Novikov, D. L. (2000). "New high-pressure phases of lithium". Nature (Springer Science and Business Media LLC) 408 (6809): 174–178. doi:10.1038/35041515. ISSN 0028-0836. PMID 11089965. Bibcode: 2000Natur.408..174H.
10. ↑ 10.00 10.01 10.02 10.03 10.04 10.05 10.06 10.07 10.08 10.09 10.10 10.11 10.12 10.13 10.14 10.15 Degtyareva, V.F. (2014). "Potassium under pressure: Electronic origin of complex structures". Solid State Sciences 36: 62–72. doi:10.1016/j.solidstatesciences.2014.07.008. Bibcode: 2014SSSci..36...62D.
11. ↑ Hanfland, M.; Loa, I.; Syassen, K. (2002-05-13). "Sodium under pressure: bcc to fcc structural transition and pressure-volume relation to 100 GPa". Physical Review B (American Physical Society (APS)) 65 (18): 184109. doi:10.1103/physrevb.65.184109. ISSN 0163-1829. Bibcode: 2002PhRvB..65r4109H.
12. ↑ McMahon, M. I.; Gregoryanz, E.; Lundegaard, L. F.; Loa, I.; Guillaume, C.; Nelmes, R. J.; Kleppe, A. K.; Amboage, M. et al. (2007-10-18). "Structure of sodium above 100 GPa by single-crystal x-ray diffraction". Proceedings of the National Academy of Sciences 104 (44): 17297–17299. doi:10.1073/pnas.0709309104. ISSN 0027-8424. PMID 17947379. Bibcode: 2007PNAS..10417297M.
13. ↑ Gregoryanz, E.; Lundegaard, L. F.; McMahon, M. I.; Guillaume, C.; Nelmes, R. J.; Mezouar, M. (2008-05-23). "Structural Diversity of Sodium". Science (American Association for the Advancement of Science (AAAS)) 320 (5879): 1054–1057. doi:10.1126/science.1155715. ISSN 0036-8075. PMID 18497293. Bibcode: 2008Sci...320.1054G.
14. ↑ Olijnyk, H.; Holzapfel, W. B. (1985-04-01). "High-pressure structural phase transition in Mg". Physical Review B (American Physical Society (APS)) 31 (7): 4682–4683. doi:10.1103/physrevb.31.4682. ISSN 0163-1829. PMID 9936412. Bibcode: 1985PhRvB..31.4682O.
15. ↑ de la Peña O’Shea, Víctor Antonio; Moreira, Iberio de P. R.; Roldán, Alberto; Illas, Francesc (8 July 2010). "Electronic and magnetic structure of bulk cobalt: The α, β, and ε-phases from density functional theory calculations". The Journal of Chemical Physics 133 (2): 024701. doi:10.1063/1.3458691. PMID 20632764.
16. ↑ 16.0 16.1 16.2 16.3 Deffrennes, Guillaume; Faure, Philippe; Bottin, François; Joubert, Jean-Marc; Oudot, Benoit (2022). "Tin (Sn) at high pressure: Review, X-ray diffraction, DFT calculations, and Gibbs energy modeling". Journal of Alloys and Compounds 919: 165675. doi:10.1016/j.jallcom.2022.165675.
17. ↑ Molodets, A. M.; Nabatov, S. S. (2000). "Thermodynamic Potentials, Diagram of State, and Phase Transitions of Tin on Shock Compression". High Temperature 38 (5): 715–721. doi:10.1007/BF02755923.
18. ↑ Benedict, U.; Haire, R. G.; Peterson, J. R.; Itie, J. P. (1985). "Delocalisation of 5f electrons in curium metal under high pressure". Journal of Physics F: Metal Physics 15 (2): L29–L35. doi:10.1088/0305-4608/15/2/002. Bibcode: 1985JPhF...15L..29B.
19. ↑ 19.0 19.1 Udayabhaskararao, Thumu; Altantzis, Thomas; Houben, Lothar; Coronado-Puchau, Marc; Langer, Judith; Popovitz-Biro, Ronit; Liz-Marzán, Luis M.; Vuković, Lela et al. (2017-10-27). "Tunable porous nanoallotropes prepared by post-assembly etching of binary nanoparticle superlattices" (in en). Science 358 (6362): 514–518. doi:10.1126/science.aan6046. ISSN 0036-8075. PMID 29074773. Bibcode: 2017Sci...358..514U.
20. ↑ 20.0 20.1 20.2 "Materials That Don't Exist in Nature Might Lead to New Fabrication Techniques" (in en-US). http://israelbds.org/materials-that-dont-exist-in-nature-might-lead-to-new-fabrication-techniques/.

## References

## External links

* Nigel Bunce and Jim Hunt. "The Science Corner: Allotropes". http://www.physics.uoguelph.ca/summer/scor/articles/scor40.htm.
* Allotropes – Chemistry Encyclopedia

0.00

(0 votes)

Original source: https://en.wikipedia.org/wiki/Allotropy. Read more

|

Retrieved from "https://handwiki.org/wiki/index.php?title=Physics:Allotropy&oldid=669606"