Titanium

Titanium [[[symbol]] Ti, atomic weight 48. (0 = 16)], a metallic chemical element. Its discovery as an element was due to William Gregor in 1789 who found in the mineral ilmenite or menachinite a new earth, which was regarded as the oxide of a new metal, menachin. Independently of him Klaproth in 1793 discovered a new metal in rutile, and called it titanium; he subsequently found that it was identical with Gregor's element. Klaproth, however, was unable to prepare the pure oxide, which was first accomplished in 1821 by Rose. The isolation of the pure metal is of much later date. Titanium, although pretty widely diffused throughout the mineral kingdom, is not found in abundance. The commonest titanium mineral is rutile or titanium dioxide, T102; anatase and brookite are crystalline allotropes. Titanium is most frequently found associated with iron; ilmenite (Ger. Titan-eisen) is FeT103, perofskite (Ca,Fe)TiO 3, and the metal occurs in most magnetic iron ores. The titanates are well marked in the mineral kingdom. Ilmenite is isomorphous with geikielite, MgTiO 3, and pyrophanite, MnTiO 3; many of the "rare minerals" - aeschynite, euxenite, polycrase, &c. - contain titanates (and also niobates). Silicates also occur; sphene or titanite, CaTiS105, is the commonest; keilhauite is rarer.

The isolation of metallic titanium is very difficult since it readily combines with nitrogen (thus resembling boron and magnesium) and carbon. In 1822 Wollaston examined a specimen of those beautiful copper-like crystals which are occasionally met with in iron-furnace slags, and declared them to be metallic titanium. This view had currency until 1849, when Wohler showed that the crystals are a compound, Ti(CN)2.3T13N2, of a cyanide and a nitride of the metal. An impure titanium was made by Wiihler and Sainte-Claire Deville in 1857 by heating to redness fluotitanate of potassium (see below) in the vapour of sodium in an atmosphere of dry hydrogen, and extracting the alkaline fluoride formed by water. The metal thus produced formed a dark brown amorphous powder resembling iron as obtained by the reduction of its oxide in hydrogen. In 1887 Nilson and Petersson (Zeit. phys. Chem. 1, p. 25) obtained a purer product by heating the chloride with sodium in a steel cylinder; it then formed yellow scales. with a bluish surface colour. H. Moissan (Compt. rend., 1895, 120, p. 290) obtained a still purer metal by igniting the oxide with carbon in the electric furnace. The product has a brilliant white fracture, a specific gravity of 4.87, very friable, but harder than quartz or steel. Moissan (ibid., 5906, 142, p. 673) has distilled this metal in a very intense electric furnace. When heated in air it burns brilliantly with the formation of the oxide. It combines directly with the halogens, and dissolves in cold dilute sulphuric acid, in hot strong hydrochloric acid and in aqua regia, but less readily in nitric acid. Its most curious property is the readiness with which it unites with nitrogen. Several nitrides have been described. Ti 3 N 4 is a copper-coloured powder obtained by heating the ammonio-chloride TiC1 4.4NH 3 in ammonia. TiN 2 is a dark blue powder obtained when the oxide is ignited in an atmosphere of ammonia; while TiN is obtained as a bronze yellow mass as hard as the diamond by heating the oxide in an atmosphere of nitrogen in the electric furnace.

In its chemical relations, titanium is generally tetravalent, and occurs in the same sub-group of the periodic classification as zirconium, cerium and thorium. It forms several oxides, TiO 2, Ti 2 O 3 and TiO 3 being the best known; others (some of doubtful existence) have been described from time to time.

Titanium dioxide, T102, occurs in nature as the three distinct mineral species rutile, brookite and anatase. Rutile assumes tetragonal forms isomorphous with cassiterite, SnO 2 (and also zircon, ZrSiO 4); anatase is also tetragonal, and brookite or thorhombic. Rutile is the most stable and anatase the least, a character reflected in the decrease in density from rutile (4.2) and brookite (4.0) to anatase (3.9). The minerals are generally found together - a feature rarely met with in the case of polymorphs. They have been obtained artificially by Hautefeuille by the interaction of titanium fluoride and steam. At a red heat rutile is produced, at the boiling point of zinc brookite, and of cadmium anatase. It is apparent that these minerals all result in nature from pneumatolytic action. Amorphous titanium oxide may be obtained in a pure form. by fusing the mineral, very finely powdered, with six times its weight of potassium bisulphate in a platinum crucible, then extracting the melt with cold water and boiling the filtered solution for a long time. Titanic oxide separates out as a white hydrate, which, however, is generally contaminated with ferric hydrate and often with tin oxide. A better method is Wohler's, in which the finely powdered mineral is fused with twice its weight of potassium carbonate in a platinum crucible, the melt powdered and treated in a platinum basin with aqueous hydrofluoric acid. The alkaline titanate first produced is converted into crystalline fluotitanate, K 2 TiF 6, which is with difficulty soluble and is extracted with hot water and filtered off. The filtrate, which may be collected in glass vessels if an excess of hydrofluoric acid has been avoided, deposits the greater part of the salt on cooling. The crystals are collected, washed, pressed and recrystallized, whereby the impurities are easily removed. The pure salt is dissolved in hot water and decomposed with ammonia to produce a slightly ammoniacal hydrated oxide; this, when ignited in platinum, leaves pure TiO 2 in the form of brownish lumps, the specific gravity of which varies from 3.9 to 4.25, according to the temperature at which it was kept in igniting. The more intense the heat the denser the product. The oxide is fusible only in the oxy-hydrogen flame. It is insoluble in all acids, except in hot concentrated sulphuric, when finely powdered. If the sulphuric acid solution be evaporated to dryness the residue, after cooling, dissolves in cold water. The solution, if boiled, deposits its titanic oxide as a hydrate called metatitanic acid, TiO(OH) 21 because it differs in its properties from orthotitanic acid, Ti(OH) 4, obtained by decomposing a solution of the chloride in cold water with alkalis. The ortho-body dissolves in cold dilute acids; the meta-body does not. If titanic oxide be fused with excess of alkaline carbonate a titanate, R 2 T103, is formed. This salt is decomposed by water with the formation of a solution of alkali free of titanium, and a residue of an acid titanate, which is insoluble in water but soluble in cold 'aqueous mineral acids. The titanates are very similar to the silicates in their tendency to assume complex forms, e.g. the potassium salts are K2T103.4H20, K2T1307.3H20 and K2T16013.2H20.

Titanium monoxide, TiO, is obtained as black prismatic crystals by heating the dioxide in the electric furnace, or with magnesium powder. Titanium sesquioxide, Ti 2 O 3, is formed by heating the dioxide in hydrogen. A hydrated form is prepared when a solution of titanic acid in hydrochloric acid is digested with copper, or when the trichloride is precipitated with alkalis. Titanium trioxide, T103, is obtained as a yellow precipitate by dropping the chloride into alcohol, adding hydrogen peroxide, and finally ammonium carbonate or potash. When shaken with potash and air it undergoes autoxidation, hydrogen peroxide being formed first, which converts the trioxide into the dioxide and possibly pertitanic acid; this acid may contain sexavalent titanium (see W. Manchotnd Richter, Ber., 1906, 39, pp. 320, 488, and also Faber, Abst. ? ourn. Chem. Soc. 1907, ii. 557.) Titanium fluoride, TiF 4, is a fuming colourless liquid boiling at 284°, obtained by distilling a mixture of titanium oxide, fluorspar and sulphuric acid; by heating barium titanofluoride, BaTiF6 (Emrich, Monats., 1904, 25, p. 907); and by the action of dry hydrofluoric acid on the chloride (Ruff and Plato, Ber., 1904, 37, p. 673). By dissolving the dioxide in hydrofluoric acid a syrupy solution is obtained which probably contains titanofluoric acid, H 2 TiF 6. The salts of this acid are well known; they are isomorphous with the silico-, stannoand zircono-fluorides. They are obtained by neutralizing the solution of the acid, or by fusing the oxide with potassium carbonate and treating the melt with hydrofluoric acid. Potassium titanofluoride, K 2 TiF 6. H 2 O, forms white, shining, monoclinic scales. When ignited in a current of hydrogen it yields tiianium trifluoride, TiF 3, as a violet powder.

Titanium ch oride, TiC1 4, is obtained as a colourless filming liquid of 1.7604 sp. gr. at o° C., boiling at 116.4° under 753.3 mm. pressure (T. E. Thorpe), by heating to dull redness an intimate dry mixture of the oxide and ignited lamp-black in dry chlorine. In the method of A. Stahler and H. Wirthwein, the titanium mineral is fused with carbon in the electric furnace, the carbides treated with chlorine, and the titanium chloride condensed. The distillate is freed from vanadium by digestion with sodium amalgam. Other methods are due to E. Vigouroux and G. Arrivaut (Abst. Journ. Chem. Soc., 1907, ii. 97, 270) and Ellis (ibid, p. 270). By passing chloroform vapour over the heated dioxide the tetradiand tri-chlorides are formed, together with the free metal and a gaseous hydride, TiH 4 (Renz, Ber., 1906, 39, p. 2 49). When dropped very cautiously into cold water it dissolves into a clear solution. According to the amount of water used, TiC1 3 OH, TiC1 2 (OH) 21 TiCI(OH) 3 or titanic acid is formed. The solution when boiled deposits most of its oxide in the meta-hydrate form. It forms addition compounds similar to those formed by stannic chloride, and combines with ammonia to form TiCl 4.8NH 3 and TiC1 4.6NH 3, both of which with liquid ammonia give titanamide, Ti(NH2)4. Titanium dichloride, TiC1 21 obtained by passing hydrogen over the trichloride at a dull red heat, is a very hygroscopic brown powder which inflames when exposed to air, and energetically decomposes water. Titanium trichloride, TiC131 forms involatile, dark violet scales, and is obtained by passing the vapour of the tetrachloride mixed with hydrogen through a red-hot tube, or by heating the tetrachloride with molecular silver to 200°. It is a powerful reducing agent.

Titanium tetrabromide, TiBr 4, is an amber-coloured crystalline mass. The tetraiodide, TiI 4, is a reddish brown mass having a metallic lustre. The di-iodide, T11 21 is obtained as black lamella by passing the vapour of the tetraiodide over heated mercury in an atmosphere of hydrogen (E. Defacqz and H. Copaux, Compt. rend., 1908, 147, p. 65). Sulphides are known corresponding to the bestknown oxides.

Titanium sesquisulphate, T12(S04)3.8H20, obtained by concentrating the violet solution formed when the metal is dissolved in sulphuric acid, is interesting since it forms a caesium alum, CsTi(S04)2.12H20. It gives the normal sulphate as a yellow, deliquescent, amorphous mass when treated with nitric acid.

Acid solutions of titanates are not precipitated by sulphuretted hydrogen; but ammonium sulphide acts on them as if it were ammonia, the sulphuretted hydrogen being liberated. Titanium oxide when fused with microcosmic salt in the oxidizing flame yields a bead which is yellowish in the heat but colourless after cooling. In the reducing flame the bead becomes violet, more readily on the addition of tin; in the presence of iron it becomes blood-red. Titanic oxides when fused on charcoal, even with potassium cyanide, yield no metal. Rose determined the atomic weight to be 47.72 (H =1). A redetermination in 1885 by T. E. Thorpe gave the value 47.7 (see Journ. Chem. Soc., 1885, p. 108).